Experimental and numerical investigation on SiC coating delamination from C/SiC composites




作者: Jingmin Jia Xufei Fang Weixu Zhang* and Xue Feng*
发表/完成日期: 2015-02-21
期刊名称: Composites Science and Technology
期卷:
相关文章:
论文简介
The delamination of SiC coating on C/SiC composites leads to severe oxidation of the carbon fibers and causes reliability problems of these composites during service. In this study, flexural test was conducted at room temperature to analyze the delamination behavior of SiC coating deposited on C/SiC substrate and finite element method (FEM) was adopted to simulate the interfacial crack between the SiC coating and the C/SiC substrate based on the experimental results. Results show that the fiber orientation has significant influence on the delamination of surface SiC coating. When the SiC coating is deposited parallel to the fiber orientation and interfacial delamination direction is along fiber direction, once delamination occurs, it inclines to propagate. However, when coating is prepared in other directions, the delamination inclines to be crested. The present analyses show that a proper combination of different fiber orientations can decrease the delamination of coating for better service of the materials in applications.
版权所有:西安交通大学 站点设计:网络信息中心 陕ICP备05001571号 联系电话:82668579 82668902 QQ群号:496666580
欢迎您访问我们的网站,您是第 位访客
推荐分辨率1024*768以上 推荐浏览器IE7 Firefox 以上