- Catalytic gasification of indole in supercritical water
- 发表刊物：
- Applied Catalysis B: Environmental
- 摘要：
- We tested Ru/C, Pt/C, Pd/C, Pt/Al2O3, Pd/Al2O3, activated carbon, and Ni–Ru/CeO2 catalysts for the gasification of indole in supercritical water. All of the materials enhanced the gasification of this nitrogencontaining compound, but the bimetallic catalyst, Ni–Ru/CeO2, showed the highest activity for producing CO and CH4 and for converting indole. We focused on this catalyst in more detail. The catalyst loading in the reactor has no effect on the H2 yield, but both CH4 and CO2 yields decrease with decreased loading. Water density has no statistically significant effect on the yield of gas products, but operating above the critical pressure of water is a prerequisite for the Ni–Ru composite catalyst to reach a high conversion of indole. The catalyst surface area and pore volume decrease from 5.91 m2 g−1 and 0.0169 cm3 g−1 to 2.86 m2 g−1 and 0.0137 cm3 g−1, respectively, after an SCWG reaction time of 180 min. NiO species were detected in both fresh and used catalysts and may be due to oxidation of the reduced Ni metal during sample preparation for XPS analysis, and/or a strong interaction between metal and support possibly leading to the formation of cationic Ni species. These results point to potential benefits of using this bimetallic catalyst for SCWG of streams with recalcitrant N-containing compounds.
- 合写作者：
- Yang Guo, Shuzhong Wang, Thomas Yeh, Phillip E. Savage
- 卷号：
- 166–167 (2015)
- 页面范围：
- 202–210
- 是否译文：
- 否
- 发表时间：
- 2014-11-21