Coal gasification is an effective way to use coal cleanly and efficiently, and coal gasification fine slag is a by-product of coal gasification with high carbon content, large specific surface area, developed pore structure and large output during production. At present, combustion has become an effective way to dispose of coal gasification fine slag on a large scale, and the coal gasification fine slag after combustion treatment can be further used for construction raw materials. In this paper, the emission characteristics of gas-phase pollutants and particulate matter under different combustion temperatures (900 degrees C, 1100 degrees C, 1300 degrees C) and combustion at-mosphere (5%, 10%, 21% O2 concentration) are studied with the drop tube furnace experimental system. By co-firing different proportions of coal gasification fine slag (10%, 20%, 30%) and raw coal, the pollutants formation law under co-firing conditions is studied. Scanning electron microscopy-energy spectroscopy (SEM-EDS) is used to characterize the apparent morphology and elemental composition of particulate samples. The measurement results of gas-phase pollutants show that the increase of furnace temperature and O2 concentration can effec-tively promote combustion and improve burnout characteristics, but the emission of gas-phase pollutants in -creases. A certain proportion (10%-30%) of coal gasification fine slag is added to the raw coal, which reduces the total emission of gas-phase pollutants (NOx and SOx). Studies on the characteristics of particulate matter for-mation show that co-firing with coal gasification fine slag in raw coal can effectively reduce submicron particle emission, and the lower fine particle emission is also detected at lower furnace temperature and oxygen con-centration. The element analysis of particulate matter formation shows that the Fe, Si and S elements content of submicron particle generated by YL (the coal gasification fine slag generated by water slurry furnace in of Shaanxi Extended China Coal Yulin Energy Chemical Co., Ltd) sample increases significantly with the increase of furnace temperature and O2 concentration, which is the main influencing factor for the increase of submicron particle. With the increase of the mixing ratio of YL sample, the content of major elements such as Fe, K and Mg of submicron particle decreases significantly, which is an important reason why the amount of the submicron particle decreases. |
(创新港)