论文名称：Insight into destabilization mechanism of Mg-based hydrides interstitially co-doped with nonmetals: A DFT study

发表刊物：The European Physical Journal B

摘要：Mg-based metal hydride is one of the most promising materials for hydrogen energy storage. However, the high thermal stability due to strong bonding effects between the atoms limits its practical application. In order to reduce the thermal stability, a method of doping double nonmetals into Mg-based system was proposed in this study. The density functional theory (DFT) calculation results showed that the thermal stabilities of both the B-N co-doped Mg-based alloy and its hydride are reduced compared with pure Mg-based system. The relative formation enthalpies of the alloy and its hydride are 0.323 and 0.595 eV atom−1, respectively. The values are much higher than those for either singly B- or N-doped Mg-based system. The more significant destabilization by doping double nonmetal elements than single element is mainly attributed to a dual effect in weakening Mg–Ni/NiH4 bonds, caused by criss-cross interactions between B–Ni and N–Mg bonds.

合写作者：Zhen Wu*, Luying Zhu, Fusheng Yang, Zaoxiao Zhang, and Serge N. Nyamsi

卷号：91(73)

页面范围：1-11

是否译文：否

发表时间：2018-05-02