ACS ami: Wafer-Scale 1T′ MoTe2 for Fast Response Self-Powered Wide-Range Photodetectors

点击次数：

发布时间：2023-06-02

发布时间：2023-06-02

文章标题：ACS ami: Wafer-Scale 1T′ MoTe2 for Fast Response Self-Powered Wide-Range Photodetectors

内容：

https://pubs.acs.org/doi/10.1021/acsami.3c05902

The semimetal-based photodetector possesses the intrinsic advantage of high response speed, low power consumption, and wide-range photoresponse. Here, we report the synthesis and application of 1 inch wafer-scale polycrystalline few layer 1T′-MoTe₂ on the SiO₂/Si substrate by employing a modified chemical vapor deposition method of predeposition of precursors. A continuous film with seamlessly stitched micrometer scale grains has been realized, and the pure 1T′ phase was confirmed by Raman spectroscopy. An asymmetric metal electrode photodetector device of Pd-MoTe₂-Au was designed and fabricated by using shadow mask-assisted UHV deposition. By measuring the self-powered photocurrent under the illumination of Xe lamp, we show that the device is sensitive to a wide spectra range (λ = 320–1200 nm) while maintaining high performance of the ON/OFF ratio (∼10³), responsivity (1.2 A/W), and specific detectivity (7.68 × 10¹² Jones). Under 450, 648, and 850 nm pulsed laser illumination, the response time achieves tens of microsecond scale. The device shows polarized photoresponse as well. Our work may promote the potential application of a self-powered high-performance photodetector based on 1T′-MoTe₂.

This work was finished mainly by the students Jiaotong Mao, Youqi Zhang and Yinuo Zhang.